High-pressure synthesis, crystal structure, and characterization of the new non-centrosymmetric terbium borate Tb3B10O17(OH)5

Herein, the high-pressure/high-temperature synthesis (11 GPa, 650 °C) of Tb3B10O17(OH)5 in a modified Walker-type multianvil device is presented. The structure of this rare-earth borate was determined by single-crystal X-ray diffraction methods and was found to crystallize orthorhombically in the space group Pmn21 (no. 31) with the unit cell parameters a = 16.2527(4), b = 4.4373(1), and c = 8.8174(2) Å. The new compound was further characterized using infrared spectroscopy, energy-dispersive X-ray spectroscopy, second harmonic generation (SHG) measurements, and temperature-dependent X-ray powder diffraction. Tb3B10O17(OH)5 decomposes to β-Tb(BO2)3 at temperatures higher than 460 °C. With increasing temperatures, the formation of μ-TbBO3 was observed, which transforms to π-TbBO3 upon cooling.