Formation mechanism of inherent spatial heterogeneity of microstructure and mechanical properties of NiTi SMA prepared by laser directed energy deposition
INTERNATIONAL JOURNAL OF EXTREME MANUFACTURING(2023)
摘要
Ni51Ti49 at.% bulk was additively manufactured by laser-directed energy deposition (DED) to reveal the microstructure evolution, phase distribution, and mechanical properties. It is found that the localized remelting, reheating, and heat accumulation during DED leads to the spatial heterogeneous distribution of columnar crystal and equiaxed crystal, a gradient distribution of Ni4Ti3 precipitates along the building direction, and preferential formation of Ni4Ti3 precipitates in the columnar zone. The austenite transformation finish temperature (A (f)) varies from -12.65 degrees C (Z = 33 mm) to 60.35 degrees C (Z = 10 mm), corresponding to tensile yield strength (sigma (0.2)) changed from 120 +/- 30 MPa to 570 +/- 20 MPa, and functional properties changed from shape memory effect to superelasticity at room temperature. The sample in the Z = 20.4 mm height has the best plasticity of 9.6% and the best recoverable strain of 4.2%. This work provided insights and guidelines for the spatial characterization of DEDed NiTi.
更多查看译文
关键词
shape memory alloy gradient functional materials,laser directed energy deposition,spatial heterogeneity,additive manufacturing,mechanical properties
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要