Solidification Principle in Large Vertical Steel Casting Under the EMS Effect

The surging demand for large high-quality rotor shafts or similar steel components in heavy industries (energy sector) poses new challenges to steelmakers. Based on the experience of conventional ingot and continuous casting, several new process concepts have been proposed, e.g., vertical continuous casting (VCC), semi-continuous casting (SCC), and segment casting (SC), but none of them are optimally put in operation. The main problems include the control of the as-cast structure and macrosegregation. Electromagnetic stirring (EMS) is necessary to obtain the center equiaxed zone, but EMS-induced multiphase flow can cause severe macrosegregation and uneven distribution of the as-cast structure between equiaxed and columnar. In this study, an advanced mixed columnar-equiaxed solidification model was used to investigate the formation of the as-cast structure and macrosegregation in an example of SCC with a large format (diameter 1 m). The main role of EMS is to create crystal fragments by fragmentation, which is regarded in this work as the only origin of equiaxed grains. The created equiaxed grains are brought by the EMS-induced (primary and secondary) flow and gravity-induced sedimentation to the central/lower part of the casting. The main goal of this study was to understand the solidification principle of SCC. In addition, a numerical parameter study by varying the EMS parameters was also performed to demonstrate the model capability towards the process optimization of SCC.