Ta-doped PrBaFe2O5 thorn d double perovskite as a high- performance electrode material for symmetrical solid oxide fuel cells
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY(2023)
摘要
Symmetrical solid oxide fuel cells (S-SOFCs) have received considerable attention due to fewer preparation steps in recent years. The PrBaFe2O5+8 (PBF) is a candidate material due to good catalytic activity and electrochemical stability. In this work, Ta-substituted PBF materials (PrBaFe2-xTaxO5+8, denoted as PBFTx, x = 0, 0.1, 0.2, 0.3) are prepared and eval-uated as symmetrical electrodes on GDC(Gd0.1Ce0.9O2-8)-YSZ(yttria-stabilized zirconia)-GDC three-layer electrolyte. The PrBaFe1.8Ta0.2O5+8 (PBFT0.2) symmetrical cell presents the lowest polarization resistance, and the value is 0.171 U cm2 and 0.503 U cm2 in air and hydrogen atmosphere at 800 degrees C, respectively. In addition, the PBFT0.2 cell shows a peak power density of 234 mW/cm2 using humidified hydrogen as fuel gas and air as oxidant at 800 degrees C, which is enhanced by 68% compared with that of PBF (138 mW/cm2). The results indicate that the strategy of Ta doping can improve the electrochemical performance of PBF and PBFT0.2 is a potential electrode for S-SOFCs.(c) 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.
更多查看译文
关键词
Symmetrical solid oxide fuel cell, Ta doping, Electrochemical performance
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要