Reversible Thermal Conductivity Modulation of Non-equilibrium (Sn1-XPbX)S by 2D-3D Structural Phase Transition above Room
ACS APPLIED ENERGY MATERIALS(2023)
摘要
We demonstrated a reversible two-dimensional (2D) to three-dimensional (3D) crystal-structure transition and associated thermal conductivity switching (K) well above room temperature (RT) in (Sn1-xPbx)S bulk polycrystals, solid solutions of 2D-layered SnS and 3D-cubic PbS. The direct phase boundary between the 2D and 3D structures does not exist in (Sn1-xPbx)S under the thermal equilibrium condition due to the solubility limit x = 0.5 in the 2D phase and x = 0.9 in the 3D phase. While, by applying a non-equilibrium synthesis process that combined a high-temperature solid-state reaction at 973 K and subsequent rapid thermal quenching to RT, the Sn solubility limit in the 3D (Sn1-xPbx)S was not changed but the Pb solubility limit was considerably expanded up to x = 0.9 in 2D (Sn1-xPbx)S. As a result, the direct 2D-3D phase boundary was formed in the Pb-rich (Sn0.2Pb0.8)S, which showed the reversible 2D-3D (3D-2D) structural phase transition at similar to 573 K (473 K). This transition temperature is much higher than that previously reported for (Sn0.5Pb0.5)Se, which requires temperatures lower than RT for the reversible structure transition. The electronic band structure change from a 2D semiconducting state to a 3D metallic state caused a 20-times increase in electron K (Kele) during the structural phase transition in the (Sn0.2Pb0.8)S. Still, Kele negligibly contributes to the total K. In contrast, the lattice K(Klat)was largely decreased by the 3D-2D structure transition due to the formation of a 2D-layered structure with strong phonon scattering, resulting in a 1.8-times modulation of the total K (K3D phase/K2D phase) at 463 K. The realization of 2D-3D structural phase transition above RT in (Sn1-xPbx)S would accelerate the development of thermal management materials through a crystal-structure dimensionality switch using non-equilibrium phase boundaries.
更多查看译文
关键词
tin sulfide, non-equilibrium synthesis, solid solution, phonon transport, thermal management
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要