Prediction Model and Mechanism for Drying Shrinkage of High-Strength Lightweight Concrete with Graphene Oxide.

The excellent performance of graphene oxide (GO) in terms of mechanical properties and durability has stimulated its application potential in high-strength lightweight concrete (HSLWC). However, more attention needs to be paid to the long-term drying shrinkage of HSLWC. This work aims to investigate the compressive strength and drying shrinkage behavior of HSLWC incorporating low GO content (0.00-0.05%), focusing on the prediction and mechanism of drying shrinkage. Results indicate the following: (1) GO can acceptably reduce slump and significantly increase specific strength by 18.6%. (2) Drying shrinkage increased by 8.6% with the addition of GO. A modified ACI209 model with a GO content factor was demonstrated to have high accuracy based on the comparison of typical prediction models. (3) GO not only refines the pores but also forms flower-like crystals, which results in the increased drying shrinkage of HSLWC. These findings provide support for the prevention of cracking in HSLWC.