Effect of B-Site Element on the Structure and Catalytic Performance for Toluene of the 3DOM CeBO3 Catalyst
Inorganic Chemistry(2023)
Abstract
A series of 3DOM cerium-based perovskite catalysts with different B-site elements were prepared by the colloidal crystal template method and excess impregnation method with Cr, Ni, and Mn as the B-site elements. The physical and chemical properties of the catalysts were investigated by X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), hydrogen temperature-programmed reduction (H2-TPR), and oxygen temperature-programmed desorption (O2-TPD) characterization techniques. The results showed that the catalyst with Mn as the B-site element had a high-quality macropore structure (pore size 200-250 nm), large specific surface area (45.26 m2/g), and abundant surface adsorbed oxygen content (Oads/Olatt = 0.46). The addition of manganese enhanced the low-temperature reducibility, and the main reduction peak was below 400 degrees C. The O2-TPD results showed that 3DOM CeMnO3 expressed the highest adsorption oxygen content. The 3DOM CeMnO3 possessed the best catalytic performance with T50% = 102 degrees C and T90% = 203 degrees C during the catalytic oxidation of toluene. Intermediate product study hinted that toluene was first converted into benzoic acid and benzaldehyde and then further degraded into small molecules. The catalyst with the best activity also exhibited good stability, and toluene degradation rate remained above 85% at 200 degrees C for more than 20 h of continuous experiments.
MoreTranslated text
Key words
3dom cebo<sub>3</sub>,toluene,catalytic performance,catalyst,b-site
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined