Effect of film thickness on the electrical transport in Co2FeAl0.5Si0.5 thin films

AIP ADVANCES(2023)

Cited 0|Views9
No score
Abstract
The effect of film thickness on the structural- and electrical-properties is investigated in Co2FeAl0.5Si0.5 (CFAS) thin films of thickness, t, in the range 12-75 nm. These films are grown by ultrahigh vacuum dc magnetron sputtering on Si(100) substrates with SiO2 buffer layer (300 nm), at the substrate temperature of 500 C. The GIXRD patterns reveal that B2 structural order decreases with increasing t. The film with t = 75 nm has sizable A2 disorder. Irrespective of t, rho(T, H = 0) goes through a minimum at T-min. An elaborate quantitative analysis of the rho(T, H = 0) data, taken over the temperature range 5 K to 300 K, demonstrates that the electron-diffuson (e-d) and weak localization (WL) effects (responsible for the negative temperature coefficient of resistivity (TCR) for T < T-min) compete with the electron-magnon (e-m) and electron-phonon (e-p) scattering (positive TCR) contributions to produce a minimum at T-min. Residual resistivity, rho(5K), and the e-d, wl, e-m and e-p scattering contributions to rho(T, H = 0), rho(e-d), rho(wl), rho(e-m) and rho(e-p), all go through a minimum at t = 50 nm. Regardless of t, the thermal renormalization of the spin-wave stiffness makes a significant contribution to rho(e-m).(c) 2023 Author(s).
More
Translated text
Key words
film thickness,thin films,electrical transport
AI Read Science
Must-Reading Tree
Example
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined