Regiospecific Poly(ethylene-co-vinyl alcohol) by ROMP of 3-Acetoxycyclooctene and Postpolymerization Modification for Barrier Material Applications

Ethylene vinyl alcohol (EVOH) is an oxygen barrier polymer used to prevent premature degradation of food, pharmaceuticals, and other products due to its semicrystallinity, strong intermolecular interactions, and consequently low free volume. EVOH is made using traditional free-radical copolymerization, which leads to little structural regularity. We utilized ringopening metathesis polymerization (ROMP) to determine how regioregularity impacts the barrier properties of EVOH-related materials. A regioregular (head-to-tail) polymer was synthesized from ROMP of 3-acetoxycyclooctene, followed by hydrogenation and deacylation to give a linear, highly regioregular EVOH (PH3OHCOE) containing the equivalent of 75 mol % ethylene units. The same process was carried out with 5-acetoxycyclooctene, but the resulting polymer (PH5OHCOE) is regiorandom. Both polymers were compared to an industry benchmark, EVOH-44, containing 44 mol % ethylene units. After processing, differential scanning calorimetry showed that the semicrystalline PH3OHCOE had a higher melting temperature and enthalpy of melting compared to semicrystalline PH5OHCOE, indicating that PH3OHCOE is more crystalline. This was confirmed by wide-angle X-ray scattering (WAXS). WAXS, rheological studies, and polarized optical microscopy showed that PH3OHCOE has a more well-defined crystal structure, a higher degree of hydrogen-bonding between -OH groups, and a higher glass transition temperature compared to PH5OHCOE. These differences were also highlighted in their tensile behavior, where PH3OHCOE and EVOH-44 exhibited brittle failure compared to the ductile behavior observed for PH5OHCOE. Oxygen barrier testing demonstrated that regioregular PH3OHCOE had an oxygen permeability more than a factor of 3 lower than regiorandom PH5OHCOE but still higher than EVOH-44, while water barrier testing showed that PH3OHCOE had the lowest water permeability, more than 6 times lower than EVOH-44. These results highlight the importance of regioregularity on the barrier properties of EVOH-like materials and show that structural regularity can lower oxygen permeability while maintaining low water permeability at the low vinyl alcohol content.