Investigation of the Properties of Multilayer Nanostructured Coating Based on the (Ti,Y,Al)N System with High Content of Yttrium

The studies are focused on the properties of the multilayer composite coating based on the (Ti,Y,Al)N system with high content of yttrium (about 40 at.%) of yttrium (Y). The hardness and elastic modulus were defined, and the resistance to fracture was studied during the scratch testing. Two cubic solid solutions (fcc phases), including c-(Ti,Y,Al)N and c-(Y,Ti,Al)N, are formed in the coating. The investigation of the wear resistance of the (Ti,Y,Al)N-coated tools during the turning of steel in comparison with the wear resistance of the tools with the based on the (Ti,Cr,Al)N system coating and the uncoated tools found a noticeable increase (by 250%-270%) in rake wear resistance. Active oxidation processes are observed in the (Ti,Y,Al)N coating during wear. It can be assumed that yttrium oxide is predominantly formed with a possible insignificant formation of titanium and aluminum oxides. At the same time, complete oxidation of c-(Y,Ti,Al)N nanolayers is not observed. Some hypotheses explaining the rather high performance of a coating with a high yttrium content are considered.