Effect of preheating on mechanical properties of a resin-based composite containing elastomeric urethane monomer.

Journal of the mechanical behavior of biomedical materials(2023)

引用 0|浏览12
暂无评分
摘要
This study investigated the effect of preheating an elastomeric urethane monomer (Exothane-24) experimental resin composite on its physicochemical properties. Two resin matrices were formulated: (a) 50 wt% Bisphenol-glycidyl methacrylate (Bis-GMA) and 50 wt% triethylene glycol dimethacrylate (TEGDMA); and (b) 20 wt% Exothane-24, 40 wt% Bis-GMA and 40 wt% TEGDMA. A photoinitiator system (0.25 wt% camphorquinone and 0.50 wt% ethyl-4-dimethylamino benzoate) and 65 wt% of the inorganic filler (20 wt% 0.05 μm silica and 80 wt% 0.7 μm BaBSiO glass) were added to both matrices. These formulations were then assigned to four groups: Exothane-24 (E); Exothane-24 plus preheating (EH); no Exothane-24 (NE); and no Exothane-24 plus preheating (NEH). NEH and EH were preheated at 69 °C. The dependent variables were as follows: film thickness (FT); polymerization shrinkage stress (PSS); gap width (GW); maximum rate of polymerization (Rp); and degree of conversion (DC). Data were statistically analyzed by two-way ANOVA and Tukey's test (α = 0.05). Preheating reduced FT for both composites. PSS and GW were significantly lower for EH, when compared with E. The DC for EH and NEH and the Rp for EH increased significantly. Preheating improved most of the physicochemical properties (FT, PSS, GW, and DC) of the experimental resin composite containing Exothane-24.
更多
查看译文
关键词
Alternative monomer,Dental composites,Luting agent,Mechanical properties,Polymerization kinetics,Preheating
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要