Synthesis of grape-seed derived carbon with high specific surface area for CO 2 selective adsorption

Nitrogen-doped porous carbons with BET surface area of 1068.2–3314.5 m 2 /g and nitrogen contents of 3.2–6.5% were prepared with solid waste grape-seed as raw material, NaNH 2 as activator and nitrogen source at low activation temperature. Super The activation mechanism of NaNH 2 on hydrothermal carbon precursors was first explored by thermodynamic analysis and TG-IR, which provided theoretical support for pore forming of carbon materials. Maximum CO 2 and CH 4 adsorption capacity at 273 K and pressure of 101 kPa was 5.42 and 1.76 mmol g −1 respectively, which are higher than those of majority of carbon derived from most solid wastes reported in literature. IAST selectivities of GS-3-450 with the largest BET surface area for CO 2 /CH 4 (40v/60v), CO 2 /N 2 (15v/85v), CH 4 /N 2 (50v/50v) were found to be 20.3, 71.4, 6.0 under 101 kPa and 298 K respectively. The competitive adsorption of GS-3-450 for CO 2 /CH 4 (40v/60v), CO 2 /N 2 (15v/85v), CH 4 /N 2 (50v/50v) gases mixture were examined through breakthrough experiments, and the results showed that the breakthrough time of CO 2 was longer than that of CH 4 and N 2 , which was beneficial to the separation of CO 2 from gases mixture. Eight cycles of CH 4 adsorption–desorption studies revealed that the material exhibited excellent recycling stability. Low temperature preparation method, excellent BET specific surface area and total pore volume, as well as excellent adsorption ability of CO 2 and CH 4 make it have a very great potential for the capture of CO 2 and CH 4 .