Effect of grain size on the core loss of nanocrystalline Fe86B13Cu1 prepared by ultra-rapid annealing
AIP ADVANCES(2023)
摘要
Nanocrystalline alloy samples with the same chemistry (Fe86B13Cu1) but with a range of mean grain sizes were prepared in order to investigate the effect of the grain size (D) on the core losses in nanocrystalline alloys. The core loss was measured on an Epstein frame in a frequency range between 10 Hz and 30 kHz. The measured core loss was separated into 3 parts, i.e. the hysteresis loss, classical eddy current loss and the excess loss. The classical eddy current loss is only a minor component due to the small thickness and moderately high electrical resistivity of the samples. Both the coercivity and the cycle hysteresis loss are found to follow roughly a D-3 dependence. The excess loss at the maximum polarization (J(m)) between 0.6 and 1.0 T is described universally by a simple power dependence of (J(m)center dot f)(n) with an exponent of about 1.4 over a wide frequency (f) range between 10 Hz to 30 kHz. The excess loss at low frequencies appears almost independent of the grain size. Thus, the grain size effect on the total loss at low frequencies is attributable to the change in the hysteresis loss which reflects the static coercivity. However, the excess loss at 30 kHz shows a clear increase with an increase in D, indicating that the excess loss also becomes influential to the grain size dependence of the total core loss at high frequencies.(c) 2023 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
更多查看译文
关键词
nanocrystalline fe86b13cu1,core loss,grain size,ultra-rapid
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要