Analysis of grain growth behavior of multicrystalline Mg2Si

Multicrystalline Mg2Si crystal with a diameter of 15 mm was grown via vertical Bridgman method. To clarify the growth mechanism of the multicrystalline structure, the grain growth behavior of the crystal was analyzed. This was carried out through segmenting grains by mean shift clustering using the light intensity profile obtained from multiple optical reflection images of the wafers and stacking the segmented images through the growth direction. Further crystal orientation measurement revealed that a grain with a higher surface energy competitively expanded to the lateral direction during crystal growth. We speculated that the growth behavior occurred because the supercooling was high enough to show difference in each grain's growth rate. This idea was supported by crystal growth simulation to show a tendency for the crystallization rate to increase toward the latter half growth stage, which is consistent with the assumption for crystal growth with high supercooling.