Synthesis and structure of high-purity BaCe0.25Mn0.75O3: an improved material for thermochemical water splitting

Solar thermochemical hydrogen production (STCH) via redox-active metal oxides is an approach for direct solar-driven hydrogen generation typically using a high-temperature redox cycle involving refractory oxides and steam. Typical cycles involve high-temperature reduction of oxides to form oxygen vacancies, followed by lower temperature reaction between oxygen vacancies and steam where the oxide is re-oxidized and the steam is reduced to hydrogen. Only a few materials have demonstrated reversible cycling under the typically harsh STCH conditions (e.g. 1500 degrees C reduction, 900 degrees C re-oxidation) and critical questions remain on the true reversibility of non-stoichiometric multi-cation oxide systems, significantly hampered by the lack of single-phase samples for these material systems. To date, most STCH processes have relied on CeO2 as a benchmark active material, but more recently, the 12R phase of BaCe0.25Mn0.75O3 (BCM) has demonstrated greater hydrogen-generation potential at lower peak temperatures. However, previous reports of 12R-BCM have included large fractions, > 10 wt%, of secondary phases, which complicate analysis of the stability and performance. A comprehensive understanding of the redox mechanism and reversibility of the process in BCM can only be achieved with nearly single-phase samples which, to date, have been difficult to produce. Here two approaches to BCM synthesis are reported: solid state and sol-gel-based routes. It is demonstrated that both routes can be tuned to produce the 12R structure with > 97 wt% yield when annealed >= 1450 degrees C. Herein synchrotron-based diffraction measurements of rhombohedral 12R-BCM enabled characterization of the anisotropy between thermal expansion along the c-axis and within the ab plane. The impact of high-temperature redox cycling on the stability and phase fraction of the 12R-BCM polytype was also investigated. These results offer two viable routes for synthesis of high-purity 12R-BCM critically needed for evaluating the efficacy of BCM as a STCH material and validate its ability to split water at lower temperatures over extended numbers of redox cycles.