Fatigue life assessment of low carbon API 5L X52 pipeline steels retired from long-term service

M.A. Beltrán-Zúñiga,D.I. Rivas-López,H.J. Dorantes-Rosales, W. González-Zapatero,C. Ferreira-Palma,V.M. López-Hirata,F. Hernández-Santiago

Engineering Failure Analysis（2023）

Cited 2|Views6
No score
Abstract
•Effect of natural aging on the fatigue strength of long-term exposure low carbon steel.•Detriment in fatigue properties of steel due to microstructural degradation.•Axial force-controlled fatigue tests in long-term exposure low carbon steels.•Natural aging as a main factor on the life of long-term exposure steels.•A ferrite-pearlite microstructure is more severely affected by natural aging.
More
Translated text
Key words
Fatigue lifetime,Long-term service,Natural aging,Pipeline steel,Mechanical properties