Research on the Hydration and Mechanical Properties of NAC-Hardened Cement under Various Activation Methods

Adding mineral admixture is one of the leading technical ways to improve the durability of cement-based materials. Nano attapulgite clay (NAC) is a unique fiber rod crystal structure that can change the physical and mechanical properties of cement-based materials, and opens up a new idea for exploring the durability of high-performance cement-based materials. This paper studied the effects of NAC on the hydration process, pore structure, and mechanical properties of a cement substrate under different activation methods. The results show that the pH value of the pore solution of cement mixed with 5% NAC high-viscosity ore (calcined) was 8.8% higher than that of the cement without NAC. The chemically bound water contents in the 1% and 3% NAC raw (calcined) cement were 14.11% and 14.04%; when the content of calcined NAC raw ore was 1%, the improvement effect on the cement hydration process is the best. The content of calcined NAC was 1%, 3%, and 5%, and the porosity of hardened cement paste was 19%, 19.04%, and 22.27% lower than that of the cement without NAC. Calcining NAC raw ore can improve cement's hydration process, promote cement's hydration reaction, and increase the compactness of hardened cement paste. The fluidity of the cement mortar mixed with calcined high-viscosity ore (D and E) at a mixing amount of 5% was reduced by 32.66% and 26.13%, respectively, compared to the ordinary specimens. The flexural strength of the cement paste mixed with calcined raw ore and high-viscosity ore at a mixing amount of 1% was generally improved by 28.40% and 17.28% compared to the cement without NAC paste. After calcination, the NAC raw ore is better than the high-clay ore in improving the mechanical properties of cement.