Cyclic stress–strain response and crystal plasticity finite element analysis of AISI 9310 steel in biaxial fatigue loading

There are still many gaps in the research on the multiaxial fatigue failure mechanism of the gear shaft. In this paper, cyclic stress-strain response and biaxial fatigue damage characteristics of gear steel AISI 9310 were investigated. The specimens showed obvious cyclic softening characteristics at all phase angles, and the softening rate was directly associated with the initiation and propagation of cracks. The fractographies at different phase angles revealed that the specimens under out-of-phase loading suffered fatigue failure caused by a single crack source on the surface, while the fatigue crack under in-phase loading was gathered together by the propagation of different crack sources. Finally, the established crystal plastic finite element model showed a good prediction of the plastic strain energy density at different phase angles, and the maximum error was 13.03%. Furthermore, a biaxial fatigue life prediction method was proposed, with a maximum error of 39.5%.