Effect of Aging Treatment on Microstructural Evolution and Mechanical Properties of the Electron Beam Cold Hearth Melting Ti-6Al-4V Alloy
MATERIALS(2022)
Abstract
Ti-6Al-4V (Ti64 or TC4) alloy is widely used in the industrial field. However, there have been few studies of the TC4 alloy melted by electron beam cold hearth melting (EBCHM) technology. Aging treatment has a considerable influence on the secondary alpha-phase in titanium alloys. Therefore, TC4 alloy melted by EBCHM technology was investigated in this study. The effect of different aging times on the microstructural evolution and mechanical properties of titanium alloy sheets was evaluated. The results showed that, with increase in aging time, the primary alpha-phase enlarged and grain globularization occurred. In addition, some transformed beta-phases disappeared. The strength and Vickers hardness of the heat-treated sheets decreased, while the plasticity increased with increase in aging time, indicating that the mechanical properties developed with evolution of the microstructure. After aging at 560 degrees C for 2 h, the properties overall were optimal. The type of fracture of the samples was ductile fracture; the dimples became larger with increase in aging time. After heat treatment, the recrystallized nucleus, substructures and HAGBs increased, while the deformed structure and LAGBs decreased. Some grains had rotated following heat treatment, indicating that anisotropy was greatly reduced.
MoreTranslated text
Key words
TC4 alloy,EBCHM,aging treatment,microstructure,mechanical properties
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined