Li2SiO3 Modification of C/LiFe0.5Mn0.5PO4 for High Performance Lithium‐Ion Batteries
ChemElectroChem(2022)
Abstract
AbstractThe carbon‐coated LiFe0.5Mn0.5PO4 (C/LFMP) and carbon‐coated LiFe0.5Mn0.5PO4@Li2SiO3 (C/LFMP‐LSO) could be successfully prepared by high temperature solid‐state reaction. Even though the crystal structure and morphology of C/LiFe0.5Mn0.5PO4 was not changed by Li2SiO3 coating, Li2SiO3 modification was able to facilitate the diffusion of lithium ions, resulting in an excellent rate performance and cyclic stability of C/LFMP‐1LSO (1 wt %). The reversible discharge specific capacities of C/LFMP‐1LSO are 157.6 mAh g−1 and 106.3 mAh g−1 at 0.1C and 10C, respectively. Meanwhile, the C/LFMP‐1LSO was cycled for 500 times at 5C with a capacity retention rate of 85.3 %. Furthermore, at a low temperature of 6 °C and 0.2C, the C/LFMP‐1LSO displayed good low temperature performance with a discharge specific capacity of 140.6 mAh g−1. Li2SiO3 coating was considered an effective way to boost the overall electrochemical performance of C/LFMP.
MoreTranslated text
Key words
lithium‐ion,modification batteries
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined