选区激光熔化Al-Zn-Mg-Sc合金组织与性能研究
Nonferrous Metals Science and Engineering（2022）
Abstract
采用选区激光熔化(SLM)技术成形Al-Zn-Mg-Sc合金.研究了激光打印参数及热处理工艺对Al-Zn-Mg-Sc合金显微组织与力学性能的影响.研究结果表明,打印态Al-Zn-Mg-Sc合金组织具有显著的各向异性特征:建造面熔池为鱼鳞状,晶粒为大尺寸柱状晶;扫描面熔池则为条带状,晶粒为小尺寸柱状晶与等轴晶.SLM成形的Al-Zn-Mg-Sc合金存在大量热裂纹,严重影响合金力学性能.但热处理后,Al-Zn-Mg-Sc合金力学性能显著提高.经过热处理后合金的维氏(HV)硬度由91.70提升至144.27,抗拉强度由183.71 MPa提升至257.53 MPa.