Effect of Sandblasting with Fluorapatite Glass-ceramic Powder and Chemical Primers/Adhesives on Shear Bond Strength of Indirect Repairing Composite to Zirconia.

OBJECTIVE:To investigate the effect of sandblasting with fluorapatite glass-ceramic (FGC) powder on zirconia surface roughness, crystallinity, and shear bond strength (SBS) of indirect repairing composite to zirconia using different primers/adhesives. METHODS:Zirconia blocks were treated as follows: no treatment (control group), blasting with 30-μm silica-coated alumina (CoJet group), and blasting with FGC powder (FGC group). The surface topography, silica content, roughness, and crystallinity of treated zirconia surfaces were analyzed by a scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), an optical profilometer, and X-ray diffraction (XRD), respectively. Four primers/adhesives (Monobond Plus, Calibra Silane, Futurabond M+, and Scotchbond Universal) were compared to bond precured resin composite to zirconia groups using Multilink Automix resin cement. Bonded specimens were thermocycled for 10,000 cycles and tested in SBS and the modes of failure were recorded. The effect of different surface treatments and primers/adhesives on SBS results were statistically analyzed using two-way ANOVA and Bonferroni post-hoc tests (α=0.05). RESULTS:Both CoJet and FGC groups showed rough surfaces with a higher content of silica in FGC, but less monoclinic crystals, compared to the CoJet group. The highest mean SBS was found in the FGC group treated with Monobond Plus compared to CoJet and Control groups. Adhesive failure was predominant in control groups, while combined failure was found in the CoJet and FGC groups regardless of the primers/adhesives employed. CONCLUSION:Sandblasting zirconia with FGC powder increased SBS of resin composite to zirconia with lower monoclinic phase transformation compared to CoJet sand. Monobond Plus reported the highest means of SBS values compared to other primers/adhesives.