Effect of Ti Substitution on the Properties of P3 Structure Na2/3Mn0.8Li0.2O2 Showing a Ribbon Superlattice

Oxygen anion redox offers an effective strategy to enhance the energy density of layered oxide positive electrodes for sodium- and lithium-ion batteries. However, lattice oxygen loss and irreversible structural transformations over the first cycle may result in large voltage hysteresis, thereby impeding practical application. Herein, ribbon superstructure ordering of Li/transition-metal-ions was applied to suppress the voltage hysteresis combined with Ti-substitution to improve the cycling stability for P3-Na0.67Li0.2Ti0.15Mn0.65O2. When both cation and anion redox reactions are utilized, Na0.67Li0.2Ti0.15Mn0.65O2 delivers a reversible capacity of 172 mA h g(-1) after 25 cycles at 10 mA g(-1) between 1.6-4.4 V vs. Na+/Na. Ex-situ X-ray diffraction data reveal that the ribbon superstructure is retained with negligible unit cell volume expansion/contraction upon sodiation/desodiation. The performance as a positive electrode for Li-ion batteries was also evaluated and P3-Na0.67Li0.2Ti0.15Mn0.65O2 delivers a reversible capacity of 180 mA h g(-1) after 25 cycles at 10 mA g(-1) when cycled vs. Li+/Li between 2.0-4.8 V.