Effects of Na 2 CO 3 on reduction mechanism and kinetics of iron during deep reduction of ilmenite concentrate
JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL(2022)
摘要
High-quality upgraded titanium slag obtained through semi-molten reduction with the addition of Na 2 CO 3 is important for the fluidizing chlorination process to produce TiO 2 pigments. The key is the effect of Na 2 CO 3 on the reduction behavior of iron. Therefore, the effects of Na 2 CO 3 on reduction mechanism and kinetics of iron during deep reduction of ilmenite concentrate were studied. The results indicated that the metallization ratio of the reduced sample increased with increasing temperature, time, and dose of Na 2 CO 3 . The addition of Na 2 CO 3 significantly accelerated the reduction of iron in the ilmenite concentrate and promoted the growth of iron particles. However, the addition of Na 2 CO 3 produced sodium iron titanates; thus, the metallization ratio of the sample decreased with an increase in the temperature and time when the temperature was above 1200 °C and the time was more than 30 min. When the doses of Na 2 CO 3 were 0, 3, and 6 wt.%, the reduction of iron was controlled by the interfacial chemical reaction, both the interfacial chemical reaction and diffusion, and diffusion, respectively, and the apparent activation energies were 134.91, 64.89, and 120.82 kJ/mol, respectively.
更多查看译文
关键词
Ilmenite concentrate, Sodium carbonate, Metallization ratio, Reduction mechanism, Kinetics
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要