Optically Controlled Coercive Field of MAPbl 3 /P(VDF-TrFE) Ferroelectric Composite Films

F erroelectric polymers, such as poly(vinylidene fluoride-trifluoroethylene)[P(VDF-TrFE) or PVTF] have attracted growing interest in developing flexible devices because of their excellent ferroelectricity and piezoelectricity. High coercive field( E c ) inherent to PVTF for switching its polarization, however, is not beneficial for practical memory or sensor device application. Different strategies, including irradiation and interface control, have been thus developed to reduce E c . Despite many efforts, a facile approach to tailoring intrinsic E c of PVTF has not been documented. In this work, an optically controlled E c was reported, which is achieved for the first time by introducing photosensitive MAPbI 3 nanocrystals into PVTF matrix. When exposed to the irradiation of 532 nm laser light, a decreased E c of the composites can be achieved reversibly by increasing the light density. The decreased level of E c increases as the MAPbI 3 content enhanced, and a 10.7% reduction of E c can be achieved in 15%(mass fraction) MAPbI 3 /PVTF samples. These results could be attributed to loading an internal stress on PVTF, which was generated by the photostriction of MAPbI 3 nanocrystals. This explanation was further supported by in-situ XRD results under irradiation of 532 nm laser light. Our findings may offer the opportunity to optically modulate the ferroelectric properties of PVTF composites for optimized device performances.