Synthesis, Structure, and Photocatalytic Activity of TiO2-Montmorillonite Composites

In the present study, TiO2-montmorillonite (MMT) composites were synthesized hydrothermally under variable conditions, including the TiO2/MMT mass ratio, reaction pH, reaction temperature, and dwelling time. These samples were determined by X-ray photoelectron spectrometry (XPS), ultraviolet-visible spectroscopy% (UV-Vis DRS), electrochemical impedance spectroscopy (EIS), transient photocurrent responses, photoluminescence (PL) spectra, electron paramagnetic resonance (EPR), and N-2 adsorption-desorption isotherms. The photocatalytic activity was evaluated as the ability to promote the visible-light-driven degradation of 30 mg/L of aqueous methylene blue, which was maximized for the composite with a TiO2 mass ratio of 30 wt% prepared at a pH of 6, a reaction temperature of 160 degrees C, and a dwelling time of 24 h (denoted as 30%-TM), which achieved a methylene blue removal efficiency of 95.6%, which was 4.9 times higher than that of pure TiO2. The unit cell volume and crystallite size of 30%-TM were 92.43 angstrom(3) and 9.28 nm, respectively, with a relatively uniform distribution of TiO2 particles on the MMT's surface. In addition, 30%-TM had a large specific surface area, a strong light absorption capacity, and a high Ti3+ content among the studied catalysts. Thus, the present study provides a basis for the synthesis of composites with controlled structures.