0.1C-11Mn medium manganese steel treated by quenching and tempering process

In this work, we developed a third-generation automobile steel with high strength and elongation of 0.1C-11Mn medium manganese steel using a simple quenching and low-temperature tempering heat treatment procedure. At different austenitisation temperatures, the microstructure and mechanical properties of manganese steel were examined. The microstructure included tempered martensite (TM), austenite, and ultra-fine-grained ferrite. The steel achieved the highest strength and elongation of 39.1GPa center dot% when it was quenched at 630 degrees C for 10 min and tempered at 450 degrees C for 5 min. In conclusion, dislocation strengthening was the primary factor to increase yield strength. At 630 degrees C, the steel achieved its best mechanical properties because of a higher austenite stability, work-hardening capability, and synergistic impact of ultra-fine-grained ferrite and martensite.