Progress on Large Diameter Single Crystal Growth of SiC
Meeting abstracts(2014)
Abstract
Large-diameter SiC single crystals are grown at II-VI by physical vapor transport (PVT). II-VI manufactures up to 150 mm diameter substrates of two types: vanadium doped semi-insulating and nitrogen doped n-type. We have previously discussed in some detail the practice of SiC crystal growth at II-VI [1], and reported on the properties of the grown crystals, including dominating defects and their evolution during growth [2]. This paper is an update on the progress of the growth of high quality large diameter substrates over the past 18 months. SiC single crystals grown by sublimation exhibit relatively high dislocation densities and may contain slightly misoriented grains. Defect data will be presented on wafers that have been characterized by etch pit density and X-ray rocking curves and topography. Resistivity was characterized by an eddy current measurement for conducting and capacitive based measurement for semi-insulating substrates. Using these methods a comparison of progress will be provided. We have achieved stacking fault and micro pipe free wafers with a typical total dislocation density of 6x103 cm-2, TSD density of ~1.2x103 cm-2, and typical BPD density of 5x102 cm-2 in 150mm substrates and 3x102 cm-2 in 100mm substrates. For semi-insulating wafers we have achieved resistivities in excess of 1E11ohms*cm. [1] A. Gupta et al., “Status of Large Diameter SiC Single Crystals”, Materials Science Forum, 2012, vol. 717-720, pp. 3-8. [2] P. Wu et al., “Defect Evolution during Growth of SiC Crystals”, J. Cryst. Growth, Vol. 310, 7-9 (2008), pp. 1804-1809.
MoreTranslated text
Key words
sic,growth
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined