Deposition of YSZ Layer by PS-PVD on Different Materials

Plasma Spray Physical Vapour Deposition (PS-PVD) method was designed for production of ceramic layer on nickel superalloys. In typical process before deposition the base material is heated by plasma up to 900 °C. In present article the yttria stabilized zirconia (YSZ) was deposited on low melting point materials: 2017A-type aluminium alloy and Cu-ETP copper. The influence of power current, process time and powder feed rate on structure and thickness of obtained coatings was analysed. During first deposition process the overheating of Al-sample was observed and as result the power current was decreased to 1600 A. In the next experimental the approx. 5 mm thick dense coating was formed. During experimental processes of YSZ deposition on copper the thickness of coating increased from approx. 5 to 22 mm. The copper-oxide layer was formed under ceramic layer. The microscopic assessment showed the difficulties in formation of columnar ceramic layer on use base materials. The obtained coating was characterized by dense structure as a result of lower plasma energy during process. The increasing of power current is not possible in the case of overheating of base material.