Study on the Sintering and Mg Composition Effect on MgB<sub>2</sub> Superconducting Bulks and Wires Synthesized by Powder-in-Sealed-Tube Method
Advanced Materials Research(2021)
Abstract
Numerous research efforts aimed at the MgB2 (Magnesium diboride) as a superconducting material due to its higher critical temperature than Nb-based superconductors such as NbTi, Nb3Sn. Nowadays MgB2 is becoming more popular as the candidate to be applied on medical devices and large-scale applications because of its full coherence lengths, improved critical current density and fields, and simple crystal structure. In this study, we fabricated the 4 mm MgB2 superconducting wires by mixing stoichiometric mole ratio of Mg: B with 1.0:2.0 and 1.1:2.0 through the Powder-In-Sealed-Tube (PIST) method to optimize high critical temperature (TC) than the conventional MgB2 bulk and wire. Furthermore, we decreased the diameter of 4 mm to 1.8 mm wire and analyze the effect of critical temperature. The specimens were sintered at a different temperature to investigate the sintering effect of MgB2 superconducting wire. The resistivity versus temperature relationship, surface morphology, and crystal phase was characterized using Cryogenic system, SEM (Scanning Electron Microscopy), and XRD (X-ray Diffractometer), respectively. We optimized the high Tc,onset for the bulk and 4 mm wire compared to other studies that are 42.1K and 40.3K respectively at 800°C sintered temperature. Finally, the results suggest that the stoichiometric ratio of MgB2 exhibited excellent feasibility to prepare conventional MgB2 superconducting wire.
MoreTranslated text
Key words
mgb<sub>2</sub>,mg composition effect,sintering,powder-in-sealed-tube
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined