Dominant acceptors in Li doped, magnetron deposited Cu₂O films

Abstract Cu2O films deposited by reactive magnetron sputtering with varying Li concentrations have been investigated by a combination of temperature-dependent Hall effect measurement and thermal admittance spectroscopy. As measured by secondary ion mass spectrometry, Li concentrations up to 5 × 1020 Li/cm3 have been achieved. Li doping significantly alters the electrical properties of Cu2O and increases hole concentration at room temperature for higher Li concentrations. Moreover, the apparent activation energy for the dominant acceptors decreases from around 0.2 eV for undoped or lightly doped Cu2O down to as low as 0.05 eV for higher Li concentrations.