Dielectric, structural and mechanical properties of thermally aged biaxially oriented polymeric substrates for flexible electronics
Polymer Degradation and Stability(2022)
Abstract
Two materials, polyethylene naphthalate (PEN) and polyethylene terephthalate (PET), which are often used as flexible substrates for electronics, were exposed to accelerated thermal aging at temperatures of 190 degrees C and 210 degrees C for 5000 and 2000 h, respectively. Changes in their thermal, dielectric, and mechanical properties were investigated. The results revealed that dielectric losses increase slower for PET than for PEN at lower aging temperatures. In contrast, at higher aging temperatures, similar behavior was observed for both materials. During aging, the dissipation factors of PET and PEN increased by one order of magnitude over those of the original states. The dielectric frequency-temperature characteristics obtained by broadband dielectric spectroscopy (BDS) shifted and indicated changes in the individual dielectric relaxation mechanisms (i.e., alpha, beta, beta*). Discoloration induced by thermal aging and quantified by ultraviolet-visible spectroscopy by the peak at 453 nm was detected primarily in the spectrum of PEN. The mechanical tensile strength of PET deteriorated considerably (10 times) after only a few hundred hours, whereas PEN was stable after even longer exposure times. It was found that all of the changes mentioned above are primarily related to the change in the crystalline-to-amorphous phase ratio, as demonstrated by differential scanning calorimetry (DSC) and supported by density measurements. (C) 2022 Elsevier Ltd. All rights reserved.
MoreTranslated text
Key words
Dielectric properties,Flexible substrates,Polyethylene naphthalate,Polyethylene terephthalate,Structural properties,Thermal aging
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined