Investigation of the Mechanical Properties of Vinylester-Based Sheet Moulding Compound (SMC) Subject to Particle Recycling

In light of climate change, fiber-reinforced plastics (FRP) are becoming increasingly important due to their lightweight construction potential. This benefit is additionally expanded on with the low cycle times, scrap rates and material costs of Sheet Moulding Compounds (SMC), making it the most often used material on the FRP market. While extensive studies regarding the recycling of SMC with unsaturated polyester-based matrices (UP-SMC) have been conducted in the past, this is not the case for vinylester-based SMC (VE-SMC). In this research, VE-SMC components were subject to a particle-recycling approach. Recyclate in the form of VE-SMC regrind was used to substitute SMC matrices during the compounding process. The dependence of the mechanical properties and failure behavior of VE-SMC containing regrind was investigated by means of microscopic and mechanical test methods for varying mass proportions of SMC regrind. Due to the addition of SMC regrind, a decreased fiber/matrix adhesion was observed. Furthermore, an increase in pore formation was observed with an increasing proportion of SMC regrind. The flexural modulus increased by 20% with a low percentage of regrind (omega(rSMC) = 10 wt.%) in comparison to virgin SMC. In contrast, the tensile properties decrease (up to 30%) with the addition of SMC regrind independent of the investigated proportions of SMC regrind.