ENHANCING HIGH-TEMPERATURE OXIDATION RESISTANCE OF TITANIUM ALLOY WITH KF110-B4C-Ag THROUGH LASER TECHNOLOGY

In this paper, the high-temperature oxidation resistant coating on the TA15 titanium alloy by laser cladding (LC) of the KF110-B4C-Ag mixed powders was analyzed in detail. The scanning electron microscope (SEM) and energy dispersive X-ray spectrometer (EDS) images indicated that a good metallurgy bond between the fabricated coating/TA15 was formed; also the fine/compact microstructure was produced after a cladding process. The oxidation mass gain of TA15 was higher than that of the coating after LC process, which were 3.72 and 0.91mg.cm(-2), respectively, at 60h, greatly enhancing the high temperature oxidation resistance.