Interfacial nitrogen modulated Z-scheme photoanode for solar water oxidation

The fabrication of heterojunctions with an appropriate energy band alignment is an attractive strategy to achieve highly efficient solar water splitting. Despite unique advantages, conventional type II heterojunctions face the problem of a relatively low redox power of the charge carriers. Although Z-scheme systems can overcome this problem, their introduction to photoelectrochemical (PEC) devices is challenging due to the specific band alignment. Herein, as an example, an ultrathin MoOxNy layer is deposited on the surface of TiO2 nanoarrays via an in situ conversion process, and the optimized MoOxNy/TiO2 sample generates a photocurrent density that is approximately 2.4 times that for pure TiO2. In addition, a similar surface modification leads to 2.5-and 2.6-fold higher photocurrent values for BiVO4 and WO3 nanostructures, respectively. Interestingly, the impedance of the MoOxNy/TiO2 photoanode is larger than that of the pure TiO2 in the dark, while illumination reverses the trend. This phenomenon, combined with the measured flat band positions, suggests a Z-scheme mechanism, which is further supported by surface potential measurements. The nitrogen (N) atoms play a major role in the boosted photoconversion efficiency for the MoOxNy/TiO2 Z-scheme heterojunction, not only enhancing the light sensitivity but, importantly, substantially promoting charge separation.