A Study on the Dual Thermo- and pH-Responsive Behaviors of Well-Defined Star-like Block Copolymers Synthesize by Combining of RAFT Polymerization and Thiol-Ene Click Reaction

A series of stimuli-responsive star-like block copolymers are synthesized via the combination of reversible addition, fragmentation chain transfer (RAFT) polymerization, and photo-initiated thiol-ene (PITE) click reaction. The controllable block ratio and block sequence, narrow distribution of molecular weight, and customized arm numbers of the star-shaped copolymers reveal the feasibility and benefits of combination of RAFT polymerization and PITE click reaction for synthesis of well-defined star-like (co)polymers. A clear insight into the relationship among the arm number, block sequence, and block ratio of the star-like block copolymers and their stimuli-responsive aggregation behavior was achieved via dynamic light scattering and UV-vis spectroscopy study. Notably, the star-like poly(acrylic acid)-b-poly(2-(dimethylamino) ethyl methacrylate) (star-PAA-b-PDMAEMA) shows higher lower critical solution temperature (LCST) compared to star-PDMAEMA-b-PAA with the same arm number and block ratio due to the inner charged PAA segments at pH > IEP. In addition, for star-like PAA-b-PDMAEMA, higher PAA content enhances the hydrophilicity of the polymer in basic solution and leads to the LCST increase, except for star-PAA(1)-b-PDMAEMA(4) at pH = 9.0 (approximate to IEP). For star-PDMAEMA-b-PAA, the PAA content shows minimal effect on their LCSTs, except for the polymer in solution with pH = 9.5, which is far from their IEP. The star-like block copolymers with well-defined structure and tunable composition, especially the facile-controlled block sequence, bring us a challenging opportunity to control the stimuli-responsive properties of star-like block copolymers.