Suppression of vacancy formation and hydrogen isotope retention in irradiated tungsten by addition of chromium

To study the effect of the content of chromium (Cr) in the tungsten (W) matrix on the vacancy formation and retention of hydrogen isotopes, the samples of the W-0.3 at.% Cr alloy were irradiated with 6.4 MeV Fe ions in the temperature range of 523–1273 K to a damage level of 0.26 displacement per atom (dpa). These displacement-damaged samples were exposed to D2 gas at a temperature of 673 K and a pressure of 100 kPa to decorate ion-induced defects with deuterium. The addition of 0.3 at.% Cr into the W matrix resulted in a significant decrease in the retention of deuterium compared to pure W after irradiation especially at high temperature (≥773 K). Positron lifetime in W-0.3 at.% Cr alloy irradiated at 1073 K was almost similar to that for non-irradiated one. These facts indicate the suppression of the formation of vacancy-type defects (monovacancies and vacancy clusters) by 0.3 at.% Cr addition, which leads to the significant reduction in deuterium retention in W-0.3 at.% Cr alloy.