Nonflammable, robust and flexible electrolytes enabled by phosphate coupled polymer-polymer for Li-metal batteries.

Liquid organic electrolytes commonly employed in commercial Li-ion batteries suffer from safety issues such as flammability and explosions. Replacing liquid electrolytes with nonflammable electrolytes has become increasingly attractive in the development of safe, high-energy Li-metal batteries (LMBs). In this work, nonflammable, robust, and flexible composite polymer-polymer electrolytes (PPEs) were successfully fabricated by flame-retardant solution casting with polyimide (PI) and polyvinylidene fluoride (PVDF). The optimized nonflammable PPEs (e.g., PPE-50) demonstrate not only good mechanical properties (i.e., a high tensile strength of 29.6 MPa with an elongation at break of 87.2%), but also high Li salts dissolubility, the former of which ensures the suppression of Li dendrites, while the latter further improves the ionic conductivity (∼1.86 × 10-4 S cm-1 at 30 °C). The resulting symmetric cells (Li|PPE-50|Li) offer excellent Li stripping and plating stability for 1000 h at 0.5 mA cm-2/0.25 mAh cm-2 and 600 h at 2.0 mA cm-2/1.0 mAh cm-2. In addition, the LiFePO4|PPE-50|Li half cells show high cycling performance (e.g., a reversible discharge capacity of 135.9 mAh g-1 after 300 cycles at 1C) and rate capability (e.g., 117.2 mAh g-1 at 4C). The PPE-50 is also compatible with a high-voltage cathode (e.g., LiNi0.5Mn0.3Co0.2O2), and the resulting batteries demonstrate long-term cycling stability with a high cut-off voltage of 4.5 V vs. Li/Li+. Because of the incorporation of a mechanically robust and thermally stable PI, a polar PVDF, and flame-retardant trimethyl phosphate (TMP) within PPEs, as well as the coordination between Li salts and TMP, and the interaction between Li salts and polymers (especially between Li bis(oxalato)borate) and PI, as well as the bis(oxalato)borate anion and PI), PPEs show great potential for practical and high-energy LMBs without safety concerns.