Size Effects in Single- and Few-Layer MoS2 Nanoflakes: Impact on Raman Phonons and Photoluminescence

The high optical absorption and emission of bidimensional MoS2 are fundamental properties for optoelectronic and biodetection applications and the opportunity to retain these properties in high quality nano-sized flakes would bring further possibilities. Here, a large set of single-layer and few-layer (2-3 layers) MoS2 flakes with size in the range from 10 nm to 20 mu m are obtained on sapphire by vapor deposition techniques and evaluated combining the information from the Raman phonons with photoluminescence (PL) and absorption bands. The flakes have triangular shape and are found to be progressively relaxed from the tensile strain imposed by the sapphire substrate as their size is reduced. An increasing hole doping as size decreases is deduced from the blue shift of the A(1g) phonon, related to charge transfer from adsorbed oxygen. No clear correlation is observed between defects density and size, therefore, doping would be favored by the preferential adsorption of oxygen at the edges of the flakes, being progressively more important as the edge/surface ratio is incremented. This hole doping also produces a shift of the PL band to higher energies, up to 60 meV. The PL intensity is not found to be correlated to the size but to the presence of defects. The trends with size for single-layer and for 2-3 layer samples are found to be similar and the synthesis method does not influence PL efficiency which remains high down to 40 nm being thus promising for nanoscale photonics.