Electrochemical Performance of Carbon-Rich Silicon Carbonitride Ceramic as Support for Sulfur Cathode in Lithium Sulfur Battery

As a promising matrix material for anchoring sulfur in the cathode for lithium-sulfur (Li-S) batteries, porous conducting supports have gained much attention. In this work, sulfur-containing C-rich SiCN composites are processed from silicon carbonitride (SiCN) ceramics, synthesized at temperatures from 800 to 1100 degrees C. To embed sulfur in the porous SiCN matrix, an easy and scalable procedure, denoted as melting-diffusion method, is applied. Accordingly, sulfur is infiltrated under solvothermal conditions at 155 degrees C into pores of carbon-rich silicon carbonitride (C-rich SiCN). The impact of the initial porosity and microstructure of the SiCN ceramics on the electrochemical performance of the synthesized SiCN-sulfur (SiCN-S) composites is analysed and discussed. A combination of the mesoporous character of SiCN and presence of a disordered free carbon phase makes the electrochemical performance of the SiCN matrix obtained at 900 degrees C superior to that of SiCN synthesized at lower and higher temperatures. A capacity value of more than 195 mAh/g over 50 cycles at a high sulfur content of 66 wt.% is achieved.