Deposition temperature dependence of thermo-spin and magneto-thermoelectric conversion in Co2MnGa films on Y3Fe5O12 and Gd3Ga5O12

We have characterized Co2MnGa (CMG) Heusler alloy films grown on Y3Fe5O12 (YIG) and Gd3Ga5O12 (GGG) substrates at different deposition temperatures and investigated thermo-spin and magneto-thermoelectric conversion properties by means of a lock-in thermography technique. X-ray diffraction, magnetization, and electrical transport measurements show that the deposition at high substrate temperatures induces the crystallized structures of CMG, while the resistivity of the CMG films on YIG (GGG) prepared at and above 500 degrees C (550 degrees C) becomes too high to measure the thermo-spin and magneto-thermoelectric effects due to large roughness, highlighting the difficulty of fabricating highly ordered continuous CMG films on garnet structures. Our lock-in thermography measurements show that the deposition at high substrate temperatures results in an increase in the current-induced temperature change for CMG/GGG and a decrease in that for CMG/YIG. The former indicates the enhancement of the anomalous Ettingshausen effect in CMG through crystallization. The latter can be explained by the superposition of the anomalous Ettingshausen effect and the spin Peltier effect induced by the positive (negative) charge-to-spin conversion for the amorphous (crystallized) CMG films. These results provide a hint to construct spin-caloritronic devices based on Heusler alloys. Published under an exclusive license by AIP Publishing.