Hybrid fibrous (PVDF-BaTiO3)/ PA-11 piezoelectric patch as an energy harvester for pacemakers

Lithium batteries have been widely used to power up implantable medical devices such as pacemakers that are often designed to treat, diagnose, and prevent different diseases. However, due to their limited capacity and lifetime, patients have to undergo a surgical procedure to replace the discharged battery. Recently, nanogenerators have been emerged and are broadly accepted since they can convert tiny biomechanical forces, such as heartbeats, into electrical energy. This study aims to manufacture a biocompatible and high-performance piezoelectric energy harvester (PEH) that is capable to be charged by the energy received from the heartbeat and store the generated voltage. In this research, a hybrid structure of poly (vinylidene fluoride) (PVDF) coupling with polyamide-11 (PA-11) was fabricated using dual electrospinning to enhance the piezoelectric properties of the intended PEH. The piezoelectric test results show an acceptable increase in nanofibers' piezoelectric sensitivity from 62.87 mV/N to 75.75 mV/N by adding 25% (v/v) of PA-11 to PVDF, indicating the synergistic effect of PVDF and PA-11. The specimen PVDF (75% v/v)-PA-11 (25% v/v) also showed the highest mechanical strength and consequently is suggested as the optimum sample. To further enhance the efficacy and sensitivity of PEH to convert the small mechanical forces into an acceptable voltage, 15% (w/w) of barium titanate (BaTiO3) nanoparticles were added to the hybrid structure. The crystallinity and mechanical strength were noticeably increased by incorporating BaTiO3 nanoparticles into the fibrous structure, leading to a piezoelectric sensitivity of 107.52 mV/N. This result lays the groundwork for producing an effective piezoelectric patch that could be used as pacemaker batteries.