Large magnetoelectric effect in BaFe12O19-(Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 particulate composite

Multiferroic composites with a large magnetoelectric response are gaining attractive interests for the design of magnetoelectric (ME) functional devices. In this work, the particulate ME composites (Ba0.85Ca0.15)(Zr0.1Ti0.9) O3-xBaFe12O19 (x=0, 0.1, 0.2, 0.3, 0.4 and 1) were prepared, and their structural, dielectric, magnetic, ferro-electric, piezoelectric properties and magnetoelectric coupling were systematically investigated. The composites consisted of only two chemically separated phases with well-bonded interface. Dielectric and impedance analyses indicated the co-contribution of grain and grain boundary to polarization. Well-saturated ferroelectric and magnetic hysteresis loops demonstrated multiferroic nature. ME response was investigated elaborately by employing magnetically induced polarization, together with measuring ME voltage coefficient and magnetodi-electric value. Specifically, a large ME coefficient of 26.78 mV/cm & BULL;Oe was achieved for x=0.3, which is higher than that in single-phase BaFe12O19 and its coupled composites.