Si2Te3 Photodetectors for Optoelectronic Integration at Telecommunication Wavelengths

IEEE Journal of Selected Topics in Quantum Electronics(2022)

引用 6|浏览4
暂无评分
摘要
High-performance two-dimensional (2D) - photodetectors with the potential for on-chip integration are desired for telecommunication applications. This work presents the photoresponse of planar silicon telluride photodetector (Si 2 Te 3 ) with under wavelengths of 1310 and 1550 nm light illuminations. We utilized mechanically exfoliated multilayered Si 2 Te 3 to fabricate back-gated phototransistor. The device with ∼ 50 nm Si 2 Te 3 flack thickness demonstrated a hole mobility of 0.36 cm 2 V −1  s −1 and photo-responsivities of 170.5 AW -1 (0.35 µW), and 12.1 AW -1 (0.25 µW) at 1310 nm and 1550 nm excitations, respectively. Furthermore, the frequency response of the device with two different metal contacts (Au/Cr and Al/Ti) was tested. The device exhibited moderate broadband response with Au/Cr metal contact of 3dB bandwidth of 1.6 MHz, while 3.8 MHz bandwidth is realized with Al/Ti metal contacts. We also demonstrated a prototype of a heterogeneously integrated Si 2 Te 3 photodetector onto a Si waveguide. The transmission losses in the waveguide were measured before and after the integration. Results demonstrated an attenuation of the optical signal by 24.3 dB and 18 dB for 1310 nm and 1550 nm wavelengths, respectively, that can attribute to the material induced losses. These findings suggest that Si 2 Te 3 is a promising 2D semiconductor material for optical communication photodetection.
更多
查看译文
关键词
2D materials,photodetectors,telecommunication wavelengths,Si-on-chip integrated
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要