Mechanism of BN-Promoting Acicular Ferrite Nucleation to Improve Heat-Affected Zone Toughness of V-N-Ti Microalloyed Offshore Steel

This study examined the effect of boron (B) on the microstructure and toughness of the simulated coarse-grained heat-affected zone (CGHAZ) of normalized vanadium microalloyed offshore steel by using the welding thermal simulation method under different heat inputs for welding. The results showed that when t(8/5) (the cooling time from 800 to 500 degrees C) increased from 14 s to 24 s, In the range of t(8/5) of 24-44 s, the impact energy of the CGHAZ rose initially and then remained constant at around 125 J at -40 degrees C, and dropped to 79 J when t(8/5) increased to 64 s. The particles (Ti,V)(C,N)-BN and BN contributed in the generation of acicular ferrite, which minimized the loss of CGHAZ toughness due to the presence of carbon. Furthermore, the microstructural parameters controlling CGHAZ toughness were the contents of the high misorientation grain boundaries and effective grain size at a tolerance angle of 15 degrees at varied heat inputs.