Structural And Magnetic Properties Of Fept-Tb Alloy Thin Films

We have studied structural and magnetic properties of (FePt)(1-x)Tb-x thin films grown at elevated temperatures on MgO(100) substrates. The incorporation of Tb into the chemically ordered L1(0) FePt lattice gives rise to considerable changes in the structural and magnetic properties, depending on the Tb content and the deposition temperature. When grown at 770 degrees C, pronounced L1(0) ordering of the initial FePt phase is present. It vanishes gradually with Tb addition, thereby forming additional crystalline Tb-Pt phases at higher Tb content. These structural changes are accompanied by a strong reduction of the perpendicular magnetic anisotropy with increasing Tb content, finally resulting in a soft magnetic material with in-plane easy-axis magnetization. Extended x-ray absorption fine-structure measurements were performed to examine the possible incorporation of Tb into the FePt lattice. Based on the number of Pt first neighbors, the transformation from the initial tetragonal L1(0) structure to the chemically disordered fcc (A1) phase with increasing Tb content could be firmly concluded. In a further sample series, FePt was grown at a lower temperature of 530 degrees C, which leads to reduced initial L1(0) chemical ordering. Adding Tb results in strong elastic stress in the lattice, eventually causing full amorphization of the film. Interestingly, in this case, a spin-reorientation transition from in-plane to out-of-plane magnetic easy axis is found at low temperatures, which is associated with an anisotropic chemical short-range order present in the amorphous phase. Furthermore, x-ray magnetic circular dichroism studies at the Fe L-3,L-2 and Tb M-5,M-4 edges for all samples reveal strong antiferromagnetic coupling between Fe and Tb, resulting in a reduction of the net magnetization of the film.