Early stages of subsurface crack and WEC formation in 100Cr6 bearing steel under RCF and hydrogen influence
International Journal of Fatigue(2022)
Abstract
•Subsurface transgranular cracks initiated from hydrogen-induced voids.•Both HEDE and HELP mechanisms favor White Etching Area formation.•Subsurface cracks form first and the WEAs develop because of crack face rubbing.•WEC is a result of subsurface transgranular crack formation.
MoreTranslated text
Key words
White Etching Crack WEC,White Etching Area WEA,Hydrogen embrittlement HE,Rolling Bearing,Rolling Contact Fatigue RCF