Microprocesses at the brass surface after impact of scanning beam of pulse-frequency ultraviolet nanosecond laser

A mode of laser heat treatment of the brass surface prior to conducting of diffusion bonding is proposed. We used the frequency-pulse radiation of a nanosecond ultraviolet laser at a pulse energy density W = 0.15 - 0.52 J/cm2. The metal sample was moved relative to a stationary laser beam along a raster trajectory (“snake”) so that adjacent spots were overlapped with an overlap ratio of ⩾ 99 %. The impact of radiation on brass was carried out in a subthreshold mode excluding crater formation. The process took place while the metal remained in a condensed state. A regular rough structure with a height of individual uplifts of the order of 1 micron was formed on the surface of the brass. article is devoted to creation of aerosolized detergent compositions, needful for use during operation of high-precision metal mirrors, as a rule, in field conditions. The created detergent compositions with inhibitory properties allow, simultaneously with carrying out the process of physicochemical cleaning of optical surface from technological impurities, to ensure its protection from the influence of adverse climatic factors during storage, transportation, installation and exploitation of the element with the possibility of its alignment. The high climatic resilience of the protective films investigated in this article, which are formed during the cleaning of the optical surface, is shown. In this case, the optical characteristics of the processed elements after climatic tests do not get worse.