Исследование влияния обработки поверхности Si-подложек на морфологию слоев GaP, полученных методом плазмохимического атомно-слоевого осаждения

Investigations of atomic-layer deposition of GaP layers on Si substrates with different orientations and with different preliminary surface treatment have been carried out. The deposition of GaP was carried out by the method of plasma enhanced atomic-layer deposition using in situ treatment in argon plasma. It was shown that at the initial stage of the growth of GaP layers on precisely oriented (100) Si substrates and with misorientation, two-dimensional growth occurs both after chemical and plasma surface treatment. Upon growth on (111) substrates, after plasma treatment of the surface, a transition to three-dimensional growth is observed, at which the size of islands reaches 30–40 nm. The smallest root-mean-square roughness of the surface of the growing GaP layers (<0.1 nm) was achieved for (100) substrates with a misorientation of 4 °. The GaP layers grown on (100) substrates had a roughness of ~ 0.1 nm, and on substrates with the (111) orientation - 0.12 nm. It was found that the surface treatment of Si substrates with the (100) orientation in hydrogen plasma leads to a slight increase in the surface roughness of growing GaP layers (0.12–0.14 nm), which is associated with the effect of inhomogeneous etching of silicon in hydrogen plasma. When treating the (100) silicon surface in argon plasma, the surface roughness does not change significantly in comparison with the chemical surface treatment. On the surface of substrates with preliminary deposition of an epitaxial Si layer with a thickness of 4 nm, the morphology of GaP layers is the same as in the case of using hydrogen plasma.