Transparent Nanocomposites With Enhanced Performances From Poly(Propylene Carbonate) And Silica

In this study, silica nanoparticles with a refractive index matching PPC and a diameter smaller than the visible light wavelength were chosen to prepare enhanced PPC/silica nanocomposites by a simple melt compounding method. The result exhibited all the nanocomposites possessed excellent transparency (about 90%), even in the nanocomposite with a silica content of 10 wt%. For PPC/silica nanocomposites, the percolation threshold was determined to be 7.5 wt% based on the dynamic rheological behavior and percolation theory. Moreover, the overall performance of the PPC-based nanocomposite with a silica content of 7.5% is the best. The optimal nanocomposite showed a Young's modulus of 3792 MPa, a yield strength of 46.5 MPa, a storage modulus of 3812 MPa and a highest temperature at maximum weight-loss rate (T-max, 309 degrees C). These characteristics are very important for potential commodity applications of PPC.